0Cr23Al5 Low Resistance Wire FeCrAl Alloy High Heat Wire Forging , Rolling , Annealing
0Cr23Al5
FeCrAl alloys are characterized by excellent oxidation resistance and very good form stability resulting in long element life.
They are typically used in electrical heating elements in industrial furnaces and home appliances.
Fe-Cr-Al alloy with high resistivity and serviceability temperature than that for NiCr alloy and also has lower price.
Forms:wire, bar, strip,sheet/plate,forging,tube/pipe,etc.
Manufacture Processs The manufacture started with producing ingot by advanced vacuum melting process. The wire production includes forging, rolling, annealing and drawing. From the ingot to the final thin wire, manufacture process is operated with high standard quality control system. There will be quality test for each batch of product, such as test to diameter tolerance, content, hardness, etc.
0Cr23Al5
Chemical Content, %
| C | P | S | Mn | Si | Cr | Ni | Al | Fe | Other | |
| Max | ||||||||||
| 0.06 | 0.025 | 0.020 | 0.50 | ≤0.6 | 20.5-23.5 | ≤0.60 | 4.2-5.3 | Balance | - | |
Mechanical Properties
| Max Continuous Service Temperature: Resisivity 20: Density: Thermal Conductivity: Coefficient of Thermal Expansion: Melting Point: Elongation: Micrographic Structure: Magnetic Property: | 1300 1.35+/-0.06ohm mm2/m 7.25g/cm3 60.2 KJ/m·h· 15.0×10-6/ (20~1000) 1500 Min 12% Ferrite magnetic |
Temperature Factor of Electrical Resistivity